Shougang höghållfast icke-orienterat elektrostål

Shougang höghållfast icke-orienterat elektriskt stål 25Swys500 35Swys500 35Swys600 35Swys900 50Swys650 65Swys600

Seriebetyg

0.25mm

25SWYS500

0.35mm

35SWYS500 / 35SWYS600 / 35SWYS900

0,50 mm

50SWYS650

0.65mm

65SWYS600
Shougang höghållfast icke-orienterat elektriskt stål 25Swys500 35Swys500 35Swys600 35Swys900 50Swys650 65Swys600

Drag

Tillämpning

New energy vehicle high-speed drive motor rotor.

Produktens fördelar

The yield strength reaches 950MPa, which is 150MPa higher than the highest yield strength of electrical steel in the world.

Effekt av ansökan

By using Shougang 35SWYS900 non-oriented electrical steel products, the motor torque increased by 11.3% and the maximum efficiency point increased by 0.7%.

Magnetiska egenskaper och mekaniska egenskaper

Grades Core loss
P1.0/400(W/kg)
Magnetic induction
B50(T)
Hardness
(HV1)
Yield strength
(MPa)
Tensile strength
(MPa)
35SWYS600 38.0 1.63 235 615 685
35SWYS900 60.0 1.54 300 940 960
Shougang höghållfast icke-orienterat elektriskt stål 25Swys500 35Swys500 35Swys600 35Swys900 50Swys650 65Swys600
Shougang höghållfast icke-orienterat elektriskt stål 25Swys500 35Swys500 35Swys600 35Swys900 50Swys650 65Swys600

Material av kiselstål i lager

Shougang höghållfast icke-orienterat elektriskt stål 25Swys500 35Swys500 35Swys600 35Swys900 50Swys650 65Swys600

Spot grossist- och detaljhandelsverksamhet

Tillverkning av rotor- och statorstackar